Wood Testing

Modulus of rupture

Modulus of rupture is the maximum load carrying capacity of a member. It is generally used in tests of bending strength to quantify the stress required to cause failure. It is reported in units of psi.
Test Method: IS: 1734 (P-11)1983, RA-2003, IS: 1708 (P-5) 1985

Modulus of elasticity

This test helps in determining the flexural stiffness and modulus of elasticity properties of wood-based materials by nondestructive testing using transverse vibration in the vertical direction.
Test Method: IS: 1734 (P-11)1983, RA-2003, IS: 1708 (P-5)1985

Internal bond strength

The purpose of this test is to design a compression shear device for easy and fast measurement of the bonded shear strength of wood-based materials.
Test Method: IS: 1734 (P-4) 1983, RA-2003

Moisture content

This test helps in determining the moisture content (MC) of solid wood, veneer, and other wood-base materials, including those that contain adhesives and chemical additives.
Test Method: IS: 1734 (P-1) 1983, RA-2003


Analyzing tree density can serve great ecological and scientific function. The tools used to accumulate this knowledge are generally uncomplicated and minimize any ensuing damage done to tree specimens.
Test Method: 1708 (P-2)1986, RA-2008

Bending strength

In bending, it is assumed that wood is linearly elastic for low values of stress, i.e., the stress and strain are proportional to each other and produce an elastic or straight-line plot on the typical stress-strain curve.
Test Method: IS: 1734 (P-11) 1983

Compression strength

The box compression test (bct) measures the compressive strength of boxes made of corrugated fiberboard as well as wooden boxes and crates. It provides a plot of deformation vs compressive force . Containers other than boxes can also be subjected to compression testing: drum, pail, etc.
Test Method:

Wood-based panels

This test helps in determining the structural panels of uniform properties within a panel. It is useful for evaluating plywood of clear, straight-grained veneers, and determining the effect of chemical or preservative treatments, construction, principal direction with respect to direction of stress, and other variables that are expected to uniformly influence the panel.
Test Method:IS: 4020 (P-1 to 16)1998


This test helps in determining the quantity of water absorbed in a specified time through the surface of an overlaid wood-based panel. The test method measures the rate of water weight gain within a controlled surface area of the overlaid panel surface when exposed to standing water.
Test Method: ASTM D 5795.

Swelling in thickness

This test helps in determining the effect of ambient environment, temperature and relative humidity, on the hygroscopic thickness swelling rate of wood fiberboard and wood fiber/polymer composites. A swelling model describing the thickness swelling process of composites exposed to water vapor conditions was developed, from which the parameter, KSR, can be used to quantify the swelling rate.
Test Method: IS: 2380 (P-17)1977, RA-203

Ability to hold a screw

The ability to hold screws in both face and edges is an important attribute of wood.
Test Method: IS: 2380 (P-14)1977, RA-2003, IS: 1708 (P-15)1986

Dimensions stability

Dimensional stability is measured by noting the length, width and thickness of the test pieces after conditioning to constant mass at 35% rh, 25°C and after conditioning at 85% rh, 25°C. The dimensional stability is expressed as the sum of the percentage changes in each dimension between these limits.
Test Method: IS: 4020 (P-3)1998

Wood quality

This test helps in determining the quality of wood. The kind of wood that is used has a lot of bearing on how long your furniture will last. It can be made of hardwood, softwood, or engineered wood.
Test Method: IS: 4020 (P-4)1998

Impact of a soft body

To ensure that cladding panels are not at undue risk of failure from typical impacts they should be tested for both hard and soft body impact resistance in accordance with the relevant British Standard.
Test Method: IS: 4020 (P-8)1998

Resistance to indentation

Indentation hardness tests are used to determine the hardness of a material to deformation.
Test Method: IS: 4020 (P-5)1998

Flush Door Shutter

Flush Door Shutters means forming a continuous surface. As the name suggests, Flush door shutters ‘flushes’ or ‘blends’ with the wall & adds a look of continuity to the wall. Flush doors are the most economical choice for builders because of their durability, dimensional accuracy, as well as freedom from warps & de-lamination when subjected to atmospheric changes.
Test Method: IS: 2202

Pre laminated particle board

This test helps in determining the resistance to steam, Dimension, Water absorption, Resistance to Crack ,Density, Swelling in water ,Adhesion of plies, Moisture, Resistance to stains, Resistance to water, Tensile strength, Screw withdrawal strength, Resistance to Cigarette burn, Modulus of rupture, Tensile strength perpendicular to surface, Tensile strength perpendicular to surface after ageing, Abrasion resistance ,Dimension, Density & density variation, Strength, Swelling due to surface absorption.
Test Method: IS: 12823

MDF / MDP Board

MDF does not contain knots or rings, making it more uniform than natural woods during cutting and in service. Medium-density fiberboard (MDF) is an engineered wood product formed by breaking down hardwood or softwood residuals into wood fibers, often in a defibrator, combining it with wax and a resin binder, and forming panels by applying high temperature and pressure. MDF is denser than plywood.
Test Method: IS: 12406 & IS: 3087

FRP / GRP door shutter

This test helps in determining the features like quality, design, weather resistant and durability.
Test Method: IS: 4020 / 14856

Ply wood

The plywood test helps in determining their usefulness and durability. They help in measuring the quantity of moisture in the wood.
Test Method: IS: 303 / 1989